    Leveling Agent

    Product name
    Application
    Processing & Use level
    Characteristics
    K7567
    Functional leveling agent
    □ Extrude after premixing<br> □ Dosage is 0.7-1.5% of total formula weight
    ■ Prevent pits, pinholes, fish eyes, etc.<br> ■ Excellent leveling performance and weather resistance, good compatibility
    K7572
    Functional leveling agent
    □ Extrude after premixing<br> □ Dosage is 0.6-1.5% of total formula weigh
    ■ Significantly improve the melt flow of the system<br> ■ Prevent pits, pinholes, fish eyes, etc.<br> ■ The coating film has excellent leveling and fullness
    SA88
    Leveling agent
    0.8-1.2% of the formula
     Applicable to various powder paint, the overall situation is good, easy to control  Promoting flow flat, significant effect .  Enhance the powder loosening, enhancing the rate of powder
    K7573
    Leveling agent
    0.6-1.5% of the formula
     Preventing defects such as pits, pinholes, and fisheyes;  Excellent leveling performance and weather resistance;  Good film appearance and recoatability.

    GMA Resins

    Product name
    Application
    Processing & Use level
    Characteristics
    SA550
    Matting agent (GMA resin)
    □ Incorporated into formula before extrusion<br> □ Epoxy value is about 700
    ■ The lowest gloss<5%(60°)<br> ■ Excellent weather resistance and anti-yellowing
    SA580
    GMA matting resin
    □ Premix with binder before extrusion<br> □ Epoxy value approx 650
    ■ Gloss range 1-10%<br> ■ Fine and smooth levelling<br> ■ Excellent impact and bending resistance
    SA300
    GMA resin
    □ Incorporated into formula before extrusion<br> □ Epoxy equivalent value is about 300
    ■ Increase the cross link density <br> ■ Improve the mechanical strength and heat resistance,chemical resistance

    Catalyst & Accelerator

    Product name
    Application
    Processing & Use level
    Characteristics
    K7318
    Low temperature curing accelerator
    □ Incorporated into formula before extrusion<br> □ 0.5-2% by weight of total formula
    ■ Reduce curing temperature,shorten curing time<br> ■ Improve leveling and anti-yellowing<br> ■ Reduce the gloss fluctuations with curring temperature
    SA316
    Curing accelerator
    □ Incorporated into formula before extrusion<br> □0.05-0.5% by weight of total formula
    ■ 100% active constituent<br> ■ Reduce curing temperature,shorten curing time
    K7312
    Low temperature curing accelerator
    □0.5-1% by weight of total formula
     Significantly improve the solvent resistance and impact resistance of the coating film.  Improve the gloss stability of polyester/GMA matting system.  Does not affect leveling and clarity of the coating film.

    Matting agents(Indoor)

    Product name
    Application
    Processing & Use level
    Characteristics
    SA2165
    Matting agent for hybrid
    □ Incorporated into formula before extrusion
    □1-5% by weight of total formula
    ■ Provide 12-70%(60°) of gloss
    ■ Wide range of applicability to polyester resins
    ■ Good flow and anti-yellowing
    SA2165D
    Matting agent for hybrid
    □ Incorporated into formula before extrusion
    □ 1-5% by weight of total formula
    ■ Provide 8-60%(60°) of gloss
    ■ Good storage stability
    ■ Lower gloss with lower usage
    K7227
    Matting agent for hybrid
    □ Incorporated into formula before extrusion
    □ 1-4.5% by weight of total formula
    ■ Provide 3-40%(60°)of gloss
    ■ Cost saveing
    ■ Improve mechanical property
    K7232
    Matting agent for hybrid
    □ Incorporated into formula before extrusion
    □ 1-5% by weight of total formula
    □ 1phw K7232 react with 2.5phw epoxy
    ■ lowest gloss approx 3%
    ■ Good levelling ,storage stability improvement
    ■ Improving applicability to polyester resins
    K7225
    Matting agent for hybrid
    □ Incorporated into formula before extrusion
    □ 1-4.5% by weight of total formula
    ■ Provide 6-60%(60°) of gloss
    ■ Excellent flow and anti-yellowing
    ■ Wide range of applicability to polyester resins Jietonda® K7225
    SA2065K
    Physical Matting Agent for Hybrid System
    □ Extruded after premixing, the dosage is 1-4.5% of total formula weight
    ■ Provides 5-70% (60 °) gloss
    ■ Good leveling and storage stability
    ■ Low resin selectivity for wide range baking
    K7237A
    Physical Matting Agent for Hybrid System
    □ Extruded after pre-mixing, the amount is 1-5% of the total weight of the formula. One part of K7233 requires 1.5 parts of E-12 epoxy
    ■ Provides a minimum of about 2% (60 °) gloss<br> ■ Excellent storage performance<br> ■ Good leveling and strong resin adaptability
    K7232D
    matting hardener for hybrid
    Incorporated into formula before extrusion 1-5% by weight of total formula 1phw K7232D react with 1.5phw epoxy
    Excellent matting effect, the lowest gloss can reach 5% (60°) Excellent leveling performance and surface fineness; Excellent storage stability ; Environmental protection and low smoke.

    Matting agents(Outdoor)

    Product name
    Application
    Processing & Use level
    Characteristics
    SA206A
    Matting agent for PES/TGIC
    □ Incorporated into formula before extrusion<br> □ 1-3% by weight of total formula
    ■ Provide 30-70%(60°) of gloss<br> ■ Good weather resistance and low usage
    K7216
    Matting agent for PES/TGIC
    □ Incorporated into formula before extrusion
    □ 2-6% by weight of total formula
    ■ Provide 10% (60°)of gloss
    ■ Good flow and excellent anti-yellowing
    ■ Low wax
    SA2061B
    Matting agent for PES/TGIC
    □ Dry blend<br> □ 1-1.5% by weight of total formula
    ■ Provide 10-40% (60°)of gloss<br> ■ Low usage and good gloss stability
    SA2068
    Matting hardener for PES/TGIC
    □ Incorporated into formula before extrusion
    □ 1-5% by weight of total formula
    ■ Provide 10%(60°) of gloss
    ■ Good flow and good film hardness
    K7217A
    Matting agent for PES/TGIC
    □ Incorporated into formula before extrusion<br> □ 1-5% by weight of total formula
    ■ Provide 16%(60°) of gloss<br> ■ Excellent gloss stability and and anti-yellowing
    K7212
    PES / TGIC system physical matting agent
    □ Extruded after pre-mixing, the dosage is 2-6% of total formula weight
    ■ Provides about 20-60% (60 °) gloss
    ■ Good gloss stability
    ■ Good leveling and anti-yellowing
    K7215
    Matting agent for PES/TGIC
    Extruded after pre-mixing, the dosage is 4-6% of total formula weight
     Provide lowest 5% (60°) gloss  Excellent leveling with good mechanical property .  Good stability for baking, recommended to use in anti-yellowing condition.

    Wax modifiers

    Product name
    Application
    Processing & Use level
    Characteristics
    K7656
    Degassing agent for powder coatings
    □ Premix with binder before extrusion
    □ 0.5-2% by weight of total formulation
    ■ Reducing surface defects such as pits and pinholes
    ■ Without affecting coating gloss and screen printing
    ■ Non-yellowing,suitable for HAA system
    SA500
    Slip and Degassing agent
    □ Incorporated into formula before extrusion
    □ 0.5-1% by weight of total formula
    ■ Improve the film appearance and anti-yellowing
    ■ Substitute of benzoin
    SA501
    Film hardening agent
    □ Incorporated into formula before extrusion
    □ 0.5-1% by weight of total formula
    ■ Improve the hardness and smoothness of film
    SA5060
    Anti foaming agent
    □ Incorporated into formula before extrusion □ or dry blend
    □ 0.5-1.5% by weight of total formula
    ■ Eliminate pinholes,bubbles and craters
    ■ Used on porous substrates,such as cast iron
    ■ cast aluminum alloys
    SA5066
    Special film hardening agent
    □ Incorporated into formula before extrusion □ or dry blend
    □ 0.5-1.5% by weight of total formula
    ■ Increasing hardness, scratch/friction resistance
    K7661
    Degassing agent for powder coatings
    □ Premix with binder before extrusion or dry belend
    □ 0.5-1.5% by weight of total formulation
    ■ High degassing efficiency
    ■ Recommended for porous substrates

    Curing agents

    Product name
    Application
    Processing & Use level
    Characteristics
    K7101
    Epoxy hardener/curing accelerator
    □ Incorporated into formula before extrusion
    □ As curing agent,e the use level is 2-4phr on epoxy resin
    ■ Excellent flow and low usage
    ■ Used as curing agent, curing @120℃/30min
    ■ Used as accelerator, curing @240℃/30s
    K7104
    Epoxy hardener
    □ Incorporated into formula before extrusion
    □ As sole curative the use level is 3-5phr on epoxy resin
    ■ Curing @ 140℃/15min or 240℃/30s
    ■ Applied for thick film coatings or FBE coatings
    ■ Good mechanical properties
    ■ Good chemical resistance
    K7108
    Epoxy hardener
    □ Incorporated into formula before extrusion
    □ As sole curative the use level is 4-6phr on epoxy resin
    ■ Curing @ 150℃/10min or 240℃/2min
    ■ Applied for thin film decorative coatings or functional epoxy powder coatings
    ■ Good film appearance and mechanical strength
    SA31
    Epoxy hardener/curing accelerator
    □ Incorporated into formula before extrusion
    □ As accelerator, use level is 0.1-0.5% on total formula
    ■ For functional or decorative powder coatings
    ■ Curing @ 140℃/30min
    SA2830
    Epoxy hardener
    □ Incorporated into formula before extrusion
    □ 3.5-4.5phr on epoxy resin
    ■ For functional or decorative powder coatings
    ■ Curing @ 180℃/15min
    SA2831
    Epoxy hardener (accelerated DICY)
    □ Incorporated into formula before extrusion
    □ 4-5phr on epoxy resin
    ■ For functional or decorative powder coatings
    ■ Curing @ 160℃/12min or 200℃/5min
    SA3120
    β-HAA hardener
    □ Incorporated into formula before extrusion
    □ Hydroxyl equivalent value is about 84
    ■ Eco-friendly,Low-toxicity,anti-yellowing
    ■ Exterior application, Substitute of TGIC
    K7150
    Closed polyisocyanate curing agent for PU powder coatings
    It is recommended to cure with hydroxyl polymer in equivalent amount (13:87 for polyester with hydroxyl value of 30; 20:80 for polyester with hydroxyl value of 50)
     Extremely high crosslink density , excellent surface hardness and chemical resistance for coating .  Excellent leveling and smoothness.  Excellent weather resistance.

    Texture agents

    Product name
    Application
    Processing & Use level
    Characteristics
    SA207
    Texture additive
    □ Incorporated into formula before extrusion
    □ 0.08-0.15% by weight of total formula
    ■ low usage
    ■ Impart sand grain finishes
    ■ Use for electrical appliances and IT equipments
    SA2072
    texture additive
    □ Incorporated into formula before extrusion
    □ 0.1-0.2% by weight of total formula
    ■ low cost
    ■ Impart sand grain finishes
    ■ For almost all kinds of powder coatings
    SA208
    Special texture additive
    □ Incorporated into formula before extrusion
    □ 3.5-5% by weight of resin
    ■ For almost all kinds of powder coatings
    ■ Impart special texture finishes such as wrinkle, reticulated, vein, embossed and grained
    K7726
    texture additive
    □ Incorporated into formula before extrusion □ 0.2-0.6% by weight of total formula
     ● It can form a sand-like coating with excellent wear resistance. ● The sand texture surface is smoother and more delicate. ● Suitable for powder coatings of any system, such as pure epoxy, epoxy/polyester, polyester/TGIC or HAA and PU.

    Charge enhancing agents

    Product name
    Application
    Processing & Use level
    Characteristics
    SA2483
    Charge enhancing agent
    □ Incorporated into formula before extrusion
    □ 0.3-0.6% by weight of total formula
    ■ Enhance the conductivity
    ■ Improve the film appearance
    ■ Anti yellowing
    SA2485
    Charge enhancing agent
    □ Incorporated into formula before extrusion
    □ 0.2-0.5% by weight of total formula
    ■ Excellent conductivity performance
    ■ Improve the film appearance and flow
    ■ Better overall performance than SA2483
    SA2486
    Charge enhancing agent
    □ Incorporated into formula before extrusion
    □ 0.2-0.4% by weight of total formula
    ■ Excellent conductivity performance
    ■ Use for both corona gun and tribo gun
    SA2487
    Charge enhancing agent
    □ Incorporated into formula before extrusion □ 0.3-1.5% by weight of total formula
    ■ No catalytic activity, does not affect the gloss of the coating and the gel time of the coating. ■ Good geothermal stability and anti-yellowing properties. ■ Does not affect powder storage stability.
    K7017
    Charge enhancing agent
    □ Incorporated into formula before extrusion □ 0.3-1.5% by weight of total formula
    ■ No catalytic activity ,so no negative effect to the gloss of coating and gel time . ■ Good thermal stability and anti-yellowing properties.

    Functional agents

    Product name
    Application
    Processing & Use level
    Characteristics
    SA516
    Pigment dispersant
    □ Incorporated into formula before extrusion
    □ 0.5-1% by weight of total formula
    ■ Good pigment dispersing ability
    ■ Provide better color strength
    K7005
    Anti-yellowing agent
    □ Extruded after premixing, the dosage is 0.3-1% of the total weight of the formula
    ■ For a variety of powder coating systems, especially HAA systems
    ■ Can significantly inhibit the yellowing of powder coatings caused by gas baking or electric baking
    K7301A
    Bonding additive
    Refer to the TDS
    ■ Improve the metal effect of coatings
    ■ Increase bonding temperature and anti caking
    ■ Reduce the dosage of metal pigments
    SA5501
    Stabilizer for metal pigment
    □ Dry blend
    □ 2-3% by weight of total formula
    ■ Inhibiting from blackening, spot-formation and loss of brilliance of metallic coatings
    ■ Improve heat resistance
    SA5502
    Dry powder flow additive
    □ Dry blend
    □ 0.1-0.5% by weight of total formula
    ■ Improving fluidity of coating powders
    ■ Anti caking
    ■ Enhancing electrostatic spray efficiency
    ■ Controlling film thickness for thin coating
    K7921
    Adhesive modifier
    Extruded after premixing, the dosage is 0.8-1.5% of the total weight of the formula
    Improve the adhesion of the coating to metal substrates such as stainless steel and galvanized sheet, improve the flexibility of the coating without affecting the weatherability
    K7010A
    Special anti-caking additive
    □ Dry blend □ 0.2-0.4% by weight of total formula
    ■ Anti caking ■ For almost all kinds of powder coatings ■ Improving fluidity of coating powders
    K7658
    surface wetting modifier
    □ Incorporated into formula before extrusion □ 0.5-2% by weight of total formula
     Good pigment and filler wetting and dispersing properties and allow to increase the amount of pigment and filler.  Good wetting performance, improve the coating fog, improve the clarity and freshness of the coating.
    K7771
    wear-resistant agent
    □ Incorporated into formula before extrusion □ 0.2-0.5% by weight of total formula
     Can form a coating with excellent wear resistance.  Especially suitable for sand texture formula.
    K7004
    Anti-yellowing agent
    □ Extruded after premixing, the dosage is 0.5-1.5% of the total weight of the formula
     Significantly improving discoloration and performance deterioration because of gas baking ;  Can be used in PES/TGIC and PES/H AA systems, etc.
    K7007
    Anti-yellowing agent
    □ Extruded after premixing, the dosage is 0.2-1% of the total weight of the formula
     Can significantly inhibit yellowing of powder coating caused by electric baking and gas baking.  Can significantly inhibit the aging of the powder coating caused by high temperature baking, can withstand high temperature baking at 220-250 ℃.
    K7010B
    Anti caking agent
    □ Dry blend □ 0.1-0.4% by weight of total formula
     Significantly improve the dry powder fluidity and construction  No harm to the leveling and mechanical properties of the coating.
    K7923
    Adhesion promoter
    Extruded after premixing, the dosage is 0.5-1.5% of the total weight of the formula
     Significantly improve the adhesion of the coating to special metal substrates such as galvanized, magnesium aluminum alloy;

    CONTACT US

    Contact us

    Order

    HOTLINE:

    +86-564-3711165
    +86-13966241417
    +86-15212888302

    Mobile version

    Search

    Add: 15 Li Dun, North Outskirts of Luan City, Anhui, P, R, China  P.C.:237158
    Tel: +86-564-3711165 , +86-564-3711777 , Whatsapp/Wechat:+86 15212888302
    Fax: +86-564-3711167

    Copyright(C)2019, Lu'An Jietonda New Material Co.,Ltd. All Rights Reserved. Supported by ChinaChemNet ChemNet Toocle Copyright Notice 备案序号:皖ICP备11004581号